Features

• Fast curing from 0°C to 40°C (32°F to 104°F)
• Application and curing under water and humid areas
• Excellent bond to a wide range of plastics, composites and metals
• Minimum substrate pretreatment needed
• Suitable for service at temperatures up to 250°C (120°F)
• Excellent ageing and weathering resistance

• Features: For Both 2050 and 2051

  • Fast to Ultra-Fast curing from -20°C to 25°C (-4°F to 75°F)
  • Max Operating Temp 284F 140C
  • Sets Dries Cures completely underwater, high moisture and high humidity
  • Resistant to higher temperatures
  • Excellent bond to a wide range of plastics, composites and metals
  • Minimal surface cleaning, prep, pretreatment needed
  • Thixotropic Gel, Non-Sagging, Non-Dripping, Non-Running
  • Excellent ageing and weathering resistance
  • Set Time: 5 minutes
  • Time to Handling Strength (25% cure) 12-15 minutes

  • Pretreatment

    The strength and durability of a bonded joint are dependent on proper treatment of the surfaces to be bonded. At the very least, joint surfaces should be cleaned with a good degreasing agent such as acetone, iso-propanol (for plastics) or other proprietary degreasing agents in order to remove all traces of oil, grease and dirt. Low-grade alcohol, gasoline, or paint thinners should never be used. The strongest and most durable joints are obtained by either mechanically abrading or chemically etching (“pickling”) the degreased surfaces. Abrading should be followed by a second degreasing treatment.

    ARALDITE® 2051 A B structural adhesive is available in cartridges incorporating mixers and can be applied as ready to use adhesive with the aid of the tool recommended by Huntsman Advanced Materials.

    Application of Adhesive

    This system is available in cartridges incorporating mixers and can be applied as ready to use adhesive with the aid of the tool recommended by Huntsman Advanced Materials. The resin hardener mix may be applied manually or robotically to the pretreated and dry joint surfaces. Huntsman s technical support group can assist the user in the selection of a suitable application method as well as suggest a variety of reputable companies that manufacture and service adhesive dispensing equipment. A layer of adhesive 0.25 mm thick will normally impart the greatest lap shear strength to the joint. The joint components should be assembled and secured in a fixed position as soon as the adhesive has been applied. For more detailed explanations regarding surface preparation and pretreatment, adhesive joint design, and the dual cartridge dispensing system, visit www.aralditeadhesives.com.

    Temperature of application: the recommended temperature application range is 0°C to 40°C (32 to 104°F). If the adhesive is used at a temperature above 40°C, because of the fact reaction, the viscosity will increase so rapidly that a good wetting of the substrate will be difficult to achieve. Therefore above 40°C (104°F), the performance of the bond may be limited. For temperature below 0°C (32°F), the Araldite® 2050 may be preferred.

    WARNING! The cure reaction can generate a high amount of heat, it is not recommended to mix large amounts of material at room temperature

    Storage

    ARALDITE® 2051 A B Adhesive should be stored in a dry place, in the original sealed containers, at temperatures between 2°C to 8°C (36°F to 46°F). Under these storage conditions, the product has a shelf life of 24 months from date of shipment from Huntsman. The product should not be exposed to direct sunlight. The product may be placed at room temperature before use, the total time at room temperature should not exceed 6 months. Long term exposure above 25°C (77°F) will reduce the shelf life of the product. The product should be never frozen.

    For additional information, consult the Technical Data Sheet (TDS) and Safety Data Sheet (SDS).